Got this as a gift second handed and would like to sharpen it and make it usable again. The serrated top part started to just break off, so I am cautious about potential metal parts in my food. Any tips welcome, thanks.

you are viewing a single comment's thread
view the rest of the comments
[–] 4 points 2 months ago (1 child)

You should never weld a knife. It will ruin the hardening and temper. Just re-profiling the existing steel is a much better idea.

  • permalink
  • fedilink
  • source
  • parent
  • hideshow 2 child comments
    •
  • [–] 1 point 2 months ago (1 child)

    I mean, you can always re-temper as well, but now I do understand that that is going well beyond the pale of just grinding the metal down.

    That being said, depending on the knife, it could have a relatively thin, harder edge and grinding it down could go into the softer core metal.

  • permalink
  • fedilink
  • source
  • parent
  • hideshow 2 child comments
    •
  • [–] 5 points 2 months ago*

    Heating, quenching, and tempering is not a great idea if it can be avoided. It stresses the metal and can introduce new weaknesses.

    And very few knives will have a softer core. That requires extra work on the knife makers part, and is rarely worth it. And there are signs you could look for during the repair and reprofiling. So a decent knife maker should be able to tell if it will be an issue.